Continuous Casting is the process whereby molten steel is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of Continuous Casting in the 1950s, steel was poured into stationary molds to form "ingots". Since then, "continuous casting" has evolved to achieve improved yield, quality, productivity and cost efficiency. Figure 1 shows some examples of continuous caster configurations.
Figure 1 - Examples of Continuous Casters
Steel from the electric or basic oxygen furnace is tapped into a ladle and taken to the continuous casting machine. The ladle is raised onto a turret that rotates the ladle into the casting position above the tundish. Referring to Figure 2, liquid steel flows out of the ladle (1) into the tundish (2), and then into a water-cooled copper mold (3). Solidification begins in the mold, and continues through the First Zone (4) and Strand Guide (5). In this configuration, the strand is straightened (6), torch-cut (8), then discharged (12) for intermediate storage or hot charged for finished rolling.
Figure 2 - General Bloom/Beam Blank Machine Configuration
1:Ladle Turret, 2:Tundish/Tundish Car, 3:Mold, 4:First Zone (Secondary Cooling), 5:Strand Guide (plus Secondary Cooling), 6:Straightener Withdrawal Units, 7:Dummy Bar Disconnect Roll, 8:Torch Cut-Off Unit, 9:Dummy Bar Storage Area, 10:Cross Transfer Table, 11:Product Identification System, 12:Product Discharge System
Figure 3 depicts a Slab Caster layout. Note the extended roller containment compared to that for a Bloom/Beam Blank (as in Figure 2), required to maintain product shape through final solidification.
Depending on the product end-use, various shapes are cast (Figure 4). In recent years, the melting/casting/rolling processes have been linked while casting a shape that substantially conforms to the finished product. The Near-Net-Shape cast section has most commonly been applied to Beams and Flat Rolled products, and results in a highly efficient operation. The complete process chain from liquid metal to finished rolling can be achieved within two hours.
Figure 3 -Slab Caster Layout
Figure 4 - Continuous Cast Shapes (sizes in millimeters)
Production and Feasibility Study
This is the first step in designing a continuous caster. First, the product end-use dictates the quality, grade and shape of the cast product (billet, bloom, slab, beam blank, and/or round). Considerations are then made based on desired annual tonnage, liquid steel availability, and anticipated operating hours. Then, the machine design considerations can be made for the number of strands and cast speeds to match the liquid metal supply from the melt shop.
Quality and grade considerations are then utilized in determining various design parameters of the casting machine such as its length, vertical height, curved or straight mold, water versus water/air secondary cooling, electromagnetic-stirring, etc.
To start a cast, the mold bottom is sealed by a steel dummy bar, which is held in place hydraulically by the Straightener Withdrawal Units (Figure 2, item 6). This bar prevents liquid steel from flowing out of the mold. The steel poured into the mold is partially solidified, producing a steel strand with a solid outer shell and a liquid core. In this primary cooling area, once the steel shell has a sufficient thickness, about 0.4 - 0.8 inches (10 to 20 mm), the Straightener Withdrawal Units are started, and proceed to withdraw the partially solidified strand out of the mold along with the dummy bar. Liquid steel continues to pour into the mold to replenish the withdrawn steel at an equal rate. The withdrawal rate depends on the cross-section, grade and quality of steel being produced, and may vary between 12 and 300 inches per minute. Casting time is typically 1.0 - 1.5 hours per heat to avoid excessive ladle heat losses.
Upon exiting the mold, the strand enters a roller containment section and secondary cooling chamber (Figure 2, items 4 & 5) in which the solidifying strand is sprayed with water, or a combination of water and air (referred to as Air-Mist) to promote solidification. This area preserves cast shape integrity and product quality. Larger cross-sections require extended roller containment (Figure 3). Once the strand is fully solidified and has passed through the Straightener Withdrawal Units, the dummy bar is disconnected, removed and stored. Following the straightener, the strand is cut into individual pieces of the following as-cast products: slabs, blooms, billets, rounds, or beam blanks, depending on machine design.
Billets have cast section sizes up to about 7 inches square. Bloom sections sizes typically range from approximately 7 inches square to about 15 inches by 23 inches. Round castings include diameters of approximately 5 to 20 inches. Slab Castings range in thickness from 2 to 16 inches, and over 100 inches wide. Beam Blanks are shaped like dog bones, and are subsequently rolled into I-Beams. The width-to-thickness ratio, referred to as the "Aspect Ratio", is used to determine the dividing line between blooms and slabs. An Aspect Ratio of 2.5:1 or greater constitutes an as-cast product referred to as a Slab.
To summarize, the casting process is comprised of the following sections:
There are two steps involved in transferring liquid steel from the ladle to the molds. First, the steel must be transferred (or teemed) from the ladle to the tundish. Next, the steel is transferred from the tundish to the molds. Tundish-to-mold steel flow regulation occurs through orifice devices of various designs: slide gates, stopper rods, or metering nozzles, the latter controlled by tundish steel level adjustment.
The shape of the tundish is typically rectangular, but delta and "T" shapes are also common. Nozzles are located along its bottom to distribute liquid steel to the molds. The tundish also serves several other key functions:
The main function of the mold is to establish a solid shell sufficient in strength to contain its liquid core upon entry into the secondary spray cooling zone. Key product elements are shape, shell thickness, uniform shell temperature distribution, defect-free internal and surface quality with minimal porosity, and few non-metallic inclusions.
The mold is basically an open-ended box structure, containing a water-cooled inner lining fabricated from a high purity copper alloy. Mold water transfers heat from the solidifying shell. The working surface of the copper face is often plated with chromium or nickel to provide a harder working surface, and to avoid copper pickup on the surface of the cast strand, which can facilitate surface cracks on the product.
Mold heat transfer is both critical and complex. Mathematical and computer modeling are typically utilized in developing a greater understanding of mold thermal conditions, and to aid in proper design and operating practices. Heat transfer is generally considered as a series of thermal resistances as follows:
Mold oscillation is necessary to minimize friction and sticking of the solidifying shell, and avoid shell tearing, and liquid steel breakouts, which can wreak havoc on equipment and machine downtime due to clean up and repairs. Friction between the shell and mold is reduced through the use of mold lubricants such as oils or powdered fluxes. Oscillation is achieved either hydraulically or via motor-driven cams or levers which support and reciprocate (or oscillate) the mold.
Mold oscillating cycles vary in frequency, stroke and pattern. However, a common approach is to employ what is called "negative strip", a stroke pattern in which the downward stroke of the cycle enables the mold to move down faster than the section withdrawal speed. This enables compressive stresses to develop in the shell that increase its strength by sealing surface fissures and porosity.
Typically, the secondary cooling system is comprised of a series of zones, each responsible for a segment of controlled cooling of the solidifying strand as it progresses through the machine. The sprayed medium is either water or a combination of air and water.
5 - Secondary Cooling
Three (3) basic forms of heat transfer occur in this region:
6 - Solidification Profile Through Steel Shell & Roll
Shell growth can be reliably predicted from Fick's Law:
This equation can be used also to calculate the casting distance (L) where the product is fully-solidified (i.e. no liquid core remaining); solving for "L":
The containment region is an integral part of the secondary cooling area. A series of retaining rolls contain the strand, extending across opposite strand faces. Edge roll containment may also be required. The focus of this area is to provide strand guidance and containment until the solidifying shell is self-supporting.
In order to avoid compromises
in product quality, careful consideration must be made to minimize stresses
associated with the roller arrangement and strand unbending. Thus, roll layout,
including spacing and roll diameters are carefully selected to minimize between-roll
bulging and liquid/solid interface strains.
Strand support requires maintaining strand shape, as the strand itself is a solidifying shell containing a liquid core, that possesses bulging ferrostatic forces from head pressure related to machine height. The area of greatest concern is high up in the machine. Here, the bulging force is relatively small, but the shell is thinner and at its weakest. To compensate for this inherent weakness and avoid shell rupturing and resulting liquid steel breakouts, the roll diameter is small with tight spacing. Just below the mold all four faces are typically supported, with only the broad faces supported at regions lower in the machine.
Bending and Straightening
Equally important to strand containment and guidance from the vertical to horizontal plane are the unbending and straightening forces. As unbending occurs, the solid shell outer radius is under tension, while the inner radius is under compression. The resulting strain is dictated by the arc radius along with the mechanical properties of the cast steel grade. If the strain along the outer radius is excessive, cracks could occur, seriously affecting the quality of the steel. These strains are typically minimized by incorporating a multi-point unbending process, in which the radii become progressively larger in order to gradually straighten the product into the horizontal plane.
Figure 7 - Curved Section of Multi-Strand
Beam Blank Caster prior to Unbending
Figure 8 - Straightener Withdrawal
Units for Strand Unbending
After straightening, the strand is transferred on roller tables to a cut off machine, which cuts the product into ordered lengths. Sectioning can be achieved either via torches or mechanical shears. Then, depending on the shape or grade, the cast section will either be placed in intermediate storage, hot-charged for finished rolling or sold as a semi-finished product. Prior to hot rolling, the product will enter a reheat furnace to adjust its thermal conditions to achieve optimum metallurgical properties and dimensional tolerances.
Continuous Casting has evolved from a batch process into a sophisticated continuous process. This transformation has occurred through understanding principles of mechanical design, heat-transfer, steel metallurgical properties and stress-strain relationships, to produce a product with excellent shape and quality. In recent years, the process has been optimized through careful integration of electro-mechanical sensors, computer-control, and production planning to provide a highly-automated system designed for the new millenium.
By Bruce Kozak &